    題名: n型鉍-硒-碲及p型鉍-銻-碲熱電材料之製作與研究
    Thermoelectric Properties of n-type Cu0.01Bi2Se0.3Te2.7 and p-type BixSb2-xTe3 (x=0.4-0.6)
    作者: 李政憲
    Lee, Cheng Hsien
    貢獻者: 陳洋元
    Chen, Yang Yuan
    李政憲
    Lee, Cheng Hsien
    關鍵詞: 熱電
    熱電材料
    鉍-硒-碲
    鉍-銻-碲
    Thermalelectric
    BiSbTe
    BiTeSe
    Spark Plasma Sintering
    日期: 2011
    上傳時間: 2012-10-30 10:45:02 (UTC+8)
    摘要: 找尋新穎的熱電材料是現在許多物理、化學以及材料學家的熱門研究，熱電材料的益處在於可將生活中所產生的廢熱轉化成電能再度利用，可應用在於熱機或是冷凍機之上。
    首先，在第一個研究之中，透過布理奇曼法在1050 ℃之下維持10個小時用以製作Cu0.01Bi2Te2.7Se0.3塊材，以及透過水熱法製造出Cu0.01Bi2Te2.7Se0.3奈米粒子，並且將兩種不同尺寸的粒子做不同比例的混合：奈米粒子(粒徑：20~100奈米)重量百分比0、10、20、30和100；接著探討火花電漿燒結法及奈米聚合物對熱電性質之影響。在實驗中發現材料中混入百分之三十的奈米粒子可提升熱電優質係數約一倍，由0.35提升至0.74。若是可以將起初塊材的熱電優質係數提升至較良好的0.7以上，再透過奈米聚合和燒結，其熱電係數在400 K左右是可以超過1的。由這個研究顯示出：火花電漿燒結以及奈米聚合是可以有效的提升熱電優質係數，其主要原因來自於成功的降低熱傳導係數並同時維持住原本所擁有的電阻率以及席貝克係數的提升，而熱傳導降低因於樣品中的奈米結構所造成的粒子邊界增加、晶格的不匹配導致抑制聲子的傳熱所形成的結果。
    第二個研究為一樣是透過布理奇曼法在750 ℃之下維持12個小時用以製作BixSb2-xTe3塊材，其中x分別為0.4、0.45、0.5以及0.6，本實驗主要為探討Bi的量對於BiSbTe所造成的影響。由結果中顯示x高於0.5和低於0.5所呈現的熱傳性質的趨勢有些許不同。在x為0.45的塊材中，得到本實驗中在室溫之下，最佳的熱電優質係數1.5，獲得此結果的主要原因來自於相對較低的電阻率，並可觀察到x為0.45的載子濃度高於0.4、0.5和0.6的結果，其將可以佐證x=0.45塊材的低電組率所造成的優質係數提升。
    Physicists, chemists and material scientists at many major universities and research institutions throughout the world are attempting to create novel materials with high thermoelectric (TE) efficiency. It will be beneficial to harvest waste heat into electrical energy. Specialty heating and cooling are other major applications for this class of new TE materials.
    In the first study, bulk and nanoparticles of Cu0.01Bi2Te2.7Se0.3 were prepared separately. The Cu0.01Bi2Te2.7Se0.3 bulk was fabricated by Bridgeman method at 1050 ℃ for 10 hrs and the nanoparticles were made through hydrothermal method. Two kinds of powders were mixed with the ratios of NPs 0, 10, 20, 30 and 100 wt% and sintered by the SPS technique to form the composite specimens. The ZT value can be enhanced over 100% from 0.35 to 0.74 for specimen with 30 wt% nanoparticles. The consequence indicates that the SPS process and mixing nanocomposite can effectively enhance ZT value. The enhancements were caused mainly by the presence of nanostructured regions existing within the samples which lowered the thermal conductivity. The phenomenon is due to the presence of significant number of grain boundaries, shorten phonon mean free path and lattice mismatch.
    For another investigation, the BixSb2-xTe3 ingots with x=0.4, 0.45, 0.5 and 0.6. were fabricated by Bridgeman method at 750 ℃ for 12 hrs. We studied the effects of amount of Bi in BixSb2-xTe3 and the SPS process on the ZT enhancement. The experiment showed that for x >0.5, the thermal property changed from a curve to a relatively linear line at the end. The best ZT is 1.5 ingot at 300 K for x=0.45 specimen. The significant ZT improvement arises from the much-reduced electric resistivity. The lowest resistivity for x=0.45 specimen is mainly due to the highest carrier concentration than those with x=0.4, 0.5 and 0.6 ingots.
    參考文獻: [1] Nicholas Wesley Gothard, The Effects of Nanoparticle Inclusions Upon The Microstructure and Thermoelectric Transport Properties of Bismuth Telluride-Based composites, Clemson University PhD thesis (2008)
    [2] J. Yang and T. Caillat,Thermoelectric Materials for Space and Automotive Power Generation, “MRS Bulletin 31, 224 (2006)
    [3] M. Tokita, Mechanism of Spark Plasma Sintering, Sumitomo Coal Mining Company Ltd, Japan
    [4] C.L. Chen, Thermoelectricity of (Bi,Sb)2Te3 nanomaterial and photothermal properties of Au nanorods, National Taiwan Normal University PhD thesis (2009)
    [5] G. Greetham, Powder Metallurgy-An Introduction
    [6] Scheele, American Chemical Society, Vol. 4, No. 7, 4283-4291(2010).
    [7] J.L. Cui,Thermoelectric properties of Cu-doped n-type(Bi2Te3)0.9-(Bi2-xCuxSe3)0.1
    (x =0–0.2) alloys, Journal of Solid State Chemistry, 180, 3583–3587(2007)
    [8] Sin-Shien Lin, et al., Journal of applide physics, 110, 093707 (2011)
    [9] Jun Jiang, et al., Scripta Materialia 52, 347–351 (2005)
    [10] Chia-Jyi Liu, et al., J. Mater. Chem., 22, 4825(2012)
    描述: 碩士
    國立政治大學
    應用物理研究所
    99755003
    100
    資料來源: http://thesis.lib.nccu.edu.tw/record/#G0997550031
    資料類型: thesis
    顯示於類別:[應用物理研究所 ] 學位論文

    文件中的檔案:

    檔案 大小格式瀏覽次數
    003101.pdf3793KbAdobe PDF2871檢視/開啟


    在政大典藏中所有的資料項目都受到原著作權保護.


    社群 sharing

    著作權政策宣告 Copyright Announcement
    1.本網站之數位內容為國立政治大學所收錄之機構典藏，無償提供學術研究與公眾教育等公益性使用，惟仍請適度，合理使用本網站之內容，以尊重著作權人之權益。商業上之利用，則請先取得著作權人之授權。
    The digital content of this website is part of National Chengchi University Institutional Repository. It provides free access to academic research and public education for non-commercial use. Please utilize it in a proper and reasonable manner and respect the rights of copyright owners. For commercial use, please obtain authorization from the copyright owner in advance.

    2.本網站之製作，已盡力防止侵害著作權人之權益，如仍發現本網站之數位內容有侵害著作權人權益情事者，請權利人通知本網站維護人員(nccur@nccu.edu.tw)，維護人員將立即採取移除該數位著作等補救措施。
    NCCU Institutional Repository is made to protect the interests of copyright owners. If you believe that any material on the website infringes copyright, please contact our staff(nccur@nccu.edu.tw). We will remove the work from the repository and investigate your claim.
    DSpace Software Copyright © 2002-2004  MIT &  Hewlett-Packard  /   Enhanced by   NTU Library IR team Copyright ©   - 回饋